Alathon® H5220
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rGQunc_Alathon-H5220.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon H5220 provides easy processing characteristics and exhibits excellent toughness properties and color as well as low odor and good processing stability. Typical applications include housewares, containers, caps and closures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) | 20 | g/10 min | ASTM D1238 |
| Spiral Flow | 2.94 | cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | 76 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1260 | MPa | |
| 1% Secant | 1000 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 26.2 | MPa | |
| Break | 13.2 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 11 | % | |
| Break | 71 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1250 | MPa | |
| 1% Secant | 1080 | MPa | |
| 2% Secant | 903 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 38 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(0.45 MPa, Unannealed) | 73.0 | °C | ASTM D648 |
| Brittleness Temperature 6 | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Peak Melting Temperature | 128 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 116 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 246 | °C | |
| Cylinder Zone 2 Temp. | 246 | °C | |
| Cylinder Zone 3 Temp. | 243 | °C | |
| Cylinder Zone 4 Temp. | 232 | °C | |
| Cylinder Zone 5 Temp. | 232 | °C | |
| Adapter Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| 5 . | Data are for control and development work and not intended for use in design or predicting performance at elevated or sub-ambient temperatures. |
| 6 . | Low Temperature; F50; Measures the number of inches of flow produced when molten resin is injected into a long, spiral channel (0.0625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440°F. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® HMN 55180 | Saudi Polymers Company | HDPE | Marlex® |
| POLYPRO® RJ6308 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Random Copolymer | POLYPRO® |
| Bolv LDPE 273-83 | Shandong Jining Bolv Chemicals Co.,Ltd | LDPE | Bolv |
| Braskem PE TX7001 | Braskem | LDPE | Braskem PE |
| Lion Idemitsu Composites PPS C-140HG | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |