WONDERLITE® PC-110L
| Category: | PC , Polycarbonate |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | WONDERLITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rG9iGr_WONDERLITE-PC-110L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WONDERLITE® PC-110L is a Polycarbonate (PC) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 10.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % | |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 77 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 3.18 mm 1 | 61.8 | MPa | ASTM D638 |
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Break | 75.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield, 3.18 mm 2 | 6.0 | % | ASTM D638 |
| Break, 3.18 mm 3 | 110 | % | ASTM D638 |
| Break | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.35 mm 4 | 2350 | MPa | ASTM D790 |
| -- 5 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 6 | 90.2 | MPa | ASTM D790 |
| -- 7 | 90.0 | MPa | ISO 178 |
| Compressive Strength | 76.5 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 75 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 3.18 mm | 850 | J/m | ASTM D256 |
| -- | 80 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed 8 | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 9 | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 127 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525 10 |
| -- | 148 | °C | ISO 306/A50 |
| -- | 143 | °C | ISO 306/B50 |
| CLTE - Flow (44 to 100°C) | 6.0E-5 to 8.0E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 30 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 2.95 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 4.0E-4 | ||
| 1 MHz | 9.0E-3 | ||
| Arc Resistance 11 | 110 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.585 | ASTM D542 | |
| Transmittance (76200 µm) | 88.0 | % | ASTM D1003 |
| Haze (81300 µm) | < 0.80 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 230 to 300 | °C | |
| Middle Temperature | 250 to 320 | °C | |
| Front Temperature | 250 to 310 | °C | |
| Mold Temperature | 70.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 6.0 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 120°C/hr |
| 9 . | 120°C/hr |
| 10 . | Rate A (50°C/h), Loading 1 (10 N) |
| 11 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AURAPENE PPTF20BK | Aurora Manufacturing Ltd | TPO | AURAPENE |
| Elastron® G G100.A80.N | Elastron USA, Inc. | SEBS | Elastron® G |
| Hysun® 697 | Ravago Manufacturing Americas, LLC | ASA | Hysun® |
| Sylvin 9993-65 Grey 9451 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ STAT-KON™ ZE0039 compound | SABIC Innovative Plastics | Polyphenylene, Unspecified | LNP™ STAT-KON™ |