Vyncolit® G865 Datasheet,Phenolic,Vyncolit N.V.-SHANGHAI SUSHENG

Message
Vyncolit G865 is a glass fiber filled phenolic molding compound with high mechanical and good thermal properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material
Appearance	Black
Forms	Particle
Processing Method	Resin transfer molding Compression molding Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.88	g/cm³	ISO 1183
Molding Shrinkage - Flow	0.10 - 0.20	%	ISO 294-4
Water Absorption (23°C, 24 hr)	0.10	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Injection Molded)	21000	MPa	ISO 527-2
Tensile Stress (Break, Injection Molded)	60.0	MPa	ISO 527-2
Tensile Strain (Break, Injection Molded)	0.45	%	ISO 527-2
Flexural Modulus (Injection Molded)	17500	MPa	ISO 178
Flexural Stress (Injection Molded)	150	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (Injection Molded)	4.5	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	10	kJ/m²	ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	210	°C	ISO 75-2/A
8.0 MPa, not annealed	190	°C	ISO 75-2/C
Linear thermal expansion coefficient			ASTM E831
Flow	2.5E-5	cm/cm/°C	ASTM E831
Lateral	3.0E-5	cm/cm/°C	ASTM E831

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	25	kV/mm	IEC 60243-1
Comparative Tracking Index	175	V	IEC 60112

Flammability	Nominal Value	Test Method
Flame Rating		UL 94
1.60 mm	V-0	UL 94
4.00 mm	V-0	UL 94

Injection	Nominal Value	Unit
Rear Temperature	60.0	°C
Middle Temperature	73.9	°C
Nozzle Temperature	87.8	°C
Processing (Melt) Temp	98.9 - 116	°C
Mold Temperature	166 - 188	°C
Injection Pressure	100 - 248	MPa
Holding Pressure	30.0 - 89.6	MPa
Back Pressure	4.83 - 15.2	MPa

Injection instructions
Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.65 to 0.85 g/cm³Post Shrinkage, ISO 2577: 0.05 to 0.15%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 200 to 220°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 180 to 200°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 20 to 30 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 25 to 35 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 140 to 160 MPaFlexural Modulus, ISO 178, Injection Molding: 16.5 to 18.5 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 0.9 to 1%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 50 to 70 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 20 to 22 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.4 to 0.5%Charpy Notched Impact Strength, ISO 179, Injection Molding: 3.5 to 5.5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 9 to 11 kJ/m²Compressive Strength, ISO 604: 190 to 220 MPa

Injection instructions

Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ISO properties listed were tested in accordance with ISO 3167The value listed as Molding Shrinkage, ISO 294-4, was tested in accordance with ISO 2577.ISO Type: PF 2 C3Powder Density, ISO 60: 0.65 to 0.85 g/cm³Post Shrinkage, ISO 2577: 0.05 to 0.15%HDT A (1.80 MPa) Unannealed, ISO 75A, Injection Molding: 200 to 220°CHDT A (8.0 MPa) Unannealed, ISO 75A, Injection Molding: 180 to 200°CCLTE, Flow (TMA), ASTM E831, Injection Molding: 20 to 30 cm^-6/cm°CCLTE, Transverse (TMA), ASTM E831, Injection Molding: 25 to 35 cm^-6/cm°CFlexural Strength, ISO 178, Injection Molding: 140 to 160 MPaFlexural Modulus, ISO 178, Injection Molding: 16.5 to 18.5 GPaStrain to failure in Flexure, ISO 178, Injection Molding: 0.9 to 1%Tensile Stress at Break, ISO 527-1,-2, Injection Molding: 50 to 70 MPaTensile Modulus, ISO 527-1,-2, Injection Molding: 20 to 22 GPaTensile Strain at Break, ISO 527-1,-2, Injection Molding: 0.4 to 0.5%Charpy Notched Impact Strength, ISO 179, Injection Molding: 3.5 to 5.5 kJ/m²Charpy Unnotched Impact Strength, ISO 179, Injection Molding: 9 to 11 kJ/m²Compressive Strength, ISO 604: 190 to 220 MPa

Category:	Phenolic , Phenolic
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	rFSn2P_Vyncolit-G865.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
POLYMAN® (ABS) HH	A. Schulman Europe	ABS	POLYMAN®
Baytec® 5340	Covestro - PUR	TSU	Baytec®
Kumho KNB 40M	Korea Kumho Petrochemical Co., Ltd.	NBR	Kumho KNB
KumhoSunny PC/ABS HAC8260H	Shanghai KumhoSunny Plastics Co., Ltd.	PC+ABS	KumhoSunny PC/ABS
LUVOCOM® 1-0890	Lehmann & Voss & Co.	Nylon 66	LUVOCOM®