Polimid B 25 GF V0A TR1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Poliblend S.p.a. |
| Trademark: | Polimid B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rDkLNt_Polimid-B-25-GF-V0A-TR1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polimid B 25 GF V0A TR1 is a Polyamide 6 (Nylon 6) material filled with 25% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, or Latin America. Primary attribute of Polimid B 25 GF V0A TR1: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8500 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 120 | MPa | |
| Break | 120 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 2.5 | % | |
| Break | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 203 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 198 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 120 | °C | |
| Vicat Softening Temperature | 218 | °C | ISO 306/A120 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 222 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 800 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | > 3.0 | hr | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Without Load |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Polypro™ J707G | Prime Polymer Co., Ltd. | PP Copolymer | Prime Polypro™ |
| Radilon® A LX 14080 2296 | Radici Plastics | Nylon 66 | Radilon® |
| Multi-Flex® TPE A4001 LC | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| CENUSIL® R 160 | Wacker Chemie AG | Silicone | CENUSIL® |
| Lupoy® GN1002FL | LG Chem Ltd. | PC | Lupoy® |