Lumid® HI5001AS
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rCXezp_Lumid-HI5001AS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumid® HI5001AS is a Polyamide + Polyolefin (Nylon+Olefin) material. It is available in Asia Pacific, Europe, Latin America, or North America for extrusion or injection molding. Important attributes of Lumid® HI5001AS are:
Typical application of Lumid® HI5001AS: Automotive |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 41.7 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 330 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 481 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 20.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm | 140 | J/m | |
| 23°C, 6.40 mm | No Break |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 90.0 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 235 to 250 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 250 to 265 | °C | |
| Processing (Melt) Temp | 250 to 265 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| STERLENE™ BMV206C | R&P (Pte.) Ltd. | TPO (POE) | STERLENE™ |
| Nylene® 5125 HS | Custom Resins Group | Nylon 66 | Nylene® |
| Fluoraz FEPM 797 | Greene, Tweed & Co. | FEP | Fluoraz |
| SD POLYCA™ LD2050-AAH14 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |
| LEXAN™ PC1800 resin | SABIC Innovative Plastics | PC | LEXAN™ |