Luran® 378P G7
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Styrolution |
| Trademark: | Luran® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rCRQzT_Luran-378P-G7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Luran 378P G7 is a glass fiber-reinforced grade (35% GF) of SAN with very high stiffness and low thermal coefficient of linear expansion. It features good chemical and weathering resistance and is suitable for extrusion and injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Apparent Density 1 | 0.85 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.10 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.25 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 93 | ||
| Ball Indentation Hardness | 240 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 9500 | MPa | |
| 1000 hr | 7500 | MPa | |
| Flexural Stress | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 17 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 4.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 108 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 104 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 109 | °C | ISO 306/B50 |
| CLTE - Flow | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.22 | W/m/K | DIN 52612 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Constant (100 Hz) | 3.50 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 7.0E-3 | ||
| 1 MHz | 0.010 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 80.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Note Message | |
|---|---|
| 1 . | With external lubricant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1390 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| TECHNO ABS R790P | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Staramide A40 | Eurostar Engineering Plastics | Nylon 66 | Staramide |
| Texalan® 2 Series 298A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 2 Series |
| Dryflex® SE 80A301 | ELASTO | TPE | Dryflex® |