Westlake LLDPE LF1050
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rCEdKx_Westlake-LLDPE-LF1050.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake LF1050 is a butene LLDPE with high stiffness suitable for cast film extrusion. This material can be used at 100% or as blending stock with LDPE or mPE. Application/Uses: Cast Film Extrusion Profile Cast Film Blend resin for GP Packaging |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, cast film | 213 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, cast film | 248 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, extruded film | 11.7 | MPa | ASTM D882 |
| TD : Yield, 25 µm, extruded film | 12.4 | MPa | ASTM D882 |
| MD : Broken, 25 µm, extruded film | 32.4 | MPa | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 21.4 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 700 | % | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 800 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Cast Film) | 90 | g | ASTM D1709A |
| Elmendorf Tear Strength 5 | ASTM D1922 | ||
| MD : 25 µm, cast film | 60 | g | ASTM D1922 |
| TD : 25 µm, cast film | 300 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45, 25.4 µm, cast film) | 90 | ASTM D2457 | |
| Haze (25.4 µm, Cast Film) | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for cast film: nominal thickness 1.0 mils; 13 lbs/die inch @ 525° F melt temperature and 70° F chill roll temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 260 - 288 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| 5 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NatureFlex™ NVS 90 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| Catalyst CT/2-LR UV | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| Hyundai EP PPF HP190 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| PLUSTEK PA301G2 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| MAXAMID™ EPDM6G14-BK | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |