PRE-ELEC® ESD 7200
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rCEVOY_PRE-ELEC-ESD-7200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® ESD 7200 is a static dissipative thermoplastic compound based on PC/ABS. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 7200 has been developed for injection moulding. The products made out of PRE-ELEC® ESD 7200 are washable, reusable and recyclable. Surface resistance values of 1e9 ohms (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. Typical applications include injection moulded technical parts used in e.g. office machines, telecommunication, electronics, medical and pharmaceutical industries, which give permanent ESD protection. PRE-ELEC® ESD 7200 can also be extruded into sheets for thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 40.0 | MPa | ASTM D638, ISO 527-2 |
| -- | 40.0 | MPa | ASTM D638 |
| 4.00 mm | 40.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 10 | % | ASTM D638, ISO 527-2 |
| Fracture | 150 | % | ASTM D638 |
| Fracture, 4.00mm | 150 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1720 | MPa | ASTM D790 |
| 4.00 mm | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 4.00 mm) | 2.94 | kJ/m² | ASTM D256 |
| Notched Izod Impact 1(23°C) | 77 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C, 4.00 mm) | No Break | ASTM D256 | |
| Unnotched Izod Impact Strength 2(23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 106 | °C | ASTM D648B, ISO 75-2/Bf |
| 1.8 MPa, not annealed | 87.2 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 87.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ASTM D1525, ISO 306/B50 3 3 |
| -- | 121 | °C | ASTM D1525, ISO 306/A50 4 4 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+11 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Static Decay | |||
| -- | sec | ESD S20.20 | |
| -- | sec | IEC 61340-5-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Injection Pressure: Medium to High |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | 标准 B (120°C/h), 载荷2 (50N) |
| 4 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA6 30V D61 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| WPP PP PPH2CF2P-White | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Amilan® CM6241M | Toray Resin Company | Nylon Copolymer | Amilan® |
| Flontech® FT-1-TUR-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| PENTAMID B GV30 H LS black | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |