Pearlthane® MAXI 12T85E
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rC3Z4A_Pearlthane-MAXI-12T85E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PEARLTHANE® MAXI 12T85E is a polyester based TPU, supplied in form of transparent, colourless pellets, featuring medium hardness, good mechanical properties and outstanding abrasion resistance. This grade is intended for extrusion applications. Applications: PEARLTHANE® MAXI D12T85E can be mainly used for making extruded profiles, hoses and films. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.21 | g/cm³ | ASTM D792 |
| 20°C | 1.21 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 86 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 5.90 | MPa | ASTM D412, ISO 527 |
| 300% strain | 10.2 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 42.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 580 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 108 | kN/m | ASTM D624 |
| -- 2 | 110 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 3 | -45.0 | °C | ISO 11357-2 |
| Melting Temperature 4 | 180 - 190 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 175 - 195 | °C | |
| Cylinder Zone 2 Temp. | 185 - 205 | °C | |
| Cylinder Zone 3 Temp. | 195 - 215 | °C | |
| Cylinder Zone 4 Temp. | 190 - 225 | °C | |
| Die Temperature | 185 - 195 | °C |
| Extrusion instructions |
|---|
| L/D Ratio: 25:1 to 30:1Screw Compression Ratio: 2:1 to 3:1Screw Speed: 12 to 60 rpm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | Method B |
| 3 . | 10°C /min |
| 4 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Roscom PVC 720-75 | Roscom, Inc. | PVC, Flexible | Roscom PVC |
| Akulon® S223-D | DSM Engineering Plastics | Nylon 66 | Akulon® |
| Durez® 32518 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Generic PTFE - Glass Fiber | Generic | PTFE | Generic |
| Huaxia Shenzhou FKM 268 | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |