EGYPTENE LL 0209 AA
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Sidpec (Sidi Kerir Petrochemicals Co.) |
| Trademark: | EGYPTENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rBvup4_EGYPTENE-LL-0209-AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LL 0209 AA is a LLDPE copolymer with butane as comonomer which contains antioxidant. It is recommended for general purpose application. It is suitable for blending with conventional LDPE. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1872-1 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 1184 | ||
| MD : Yield | 10.0 | MPa | ISO 1184 |
| TD : Yield | 11.0 | MPa | ISO 1184 |
| MD : Fracture | 41.0 | MPa | ISO 1184 |
| TD : Fracture | 32.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Fracture | 620 | % | ISO 1184 |
| TD : Fracture | 840 | % | ISO 1184 |
| Dart Drop Impact | 150 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 150 | g | ASTM D1922 |
| TD : 25 µm | 370 | g | ASTM D1922 |
| Additional Information |
|---|
| Film properties were measured on 38 micron film extruded at a blow up ratio 2:1 with a melt temperature of 225°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ NN-20CF/000 Black | PolyOne Corporation | Nylon 66 | Stat-Tech™ |
| XANTAR® SF 2220 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| Desmopan® DP 89043D | Covestro - PUR | TPU-Polyether | Desmopan® |
| DOMAMID® A1-004-V40-N | DOMO Engineering Plastics GmbH | Nylon 6 | DOMAMID® |
| POLYabs R00 UV4 | Polykemi AB | ABS | POLYabs |