Zytel® 70G35HSRX BK099
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rAN16T_Zytel-70G35HSRX-BK099.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% Glass Reinforced, Heat Stabilized, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 5.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 285 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12000 | 9000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 5.5 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 8500 | MPa | |
| 1000 hr | -- | 6500 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 10 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 70 | kJ/m² | |
| 23°C | 80 | 100 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 6.00 | -- | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 261 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.7E-5 | -- | cm/cm/°C | |
| Transverse | 8.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.700 mm | HB | -- | ||
| 1.50 mm | HB | -- |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 1.24 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2130 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.24 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP H1501 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Sup-tech C703 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC | Sup-tech |
| VENELENE® 2811 | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| Formolene® HB5202B2 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Glastic® 1444 | Glastic Corporation | Polyester, TS | Glastic® |