Shuman PC SP910
| Category: | PC , Polycarbonate |
| Manufacturer: | Shuman Plastics, Inc. |
| Trademark: | Shuman PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | rA1mOq_Shuman-PC-SP910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYCARBONATE SP910 UTILITY BLACK OFFERS THIS COMBINATION OF PROPERTIES:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 15 - 25 | g/10 min | ASTM D1238 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 65.5 | MPa | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 128 | °C | ASTM D648 |
| Vicat Softening Temperature | 154 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.57 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 127 | °C | |
| Drying Time | 2.0 - 24 | hr | |
| Processing (Melt) Temp | 266 - 288 | °C |
| Injection instructions |
|---|
| Tray Dryer Drying Temperature, No Standard, 1.5 in: 250 to 260°FTray Dryer Drying Time, No Standard, 1.5 in: 4 to 24hrs |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 127 | °C | |
| Drying Time | 2.0 - 24 | hr | |
| Melt Temperature | 266 - 288 | °C |
| Extrusion instructions |
|---|
| Tray Dryer Drying Temperature, No Standard, 1.5 in: 250 to 260°FTray Dryer Drying Time, No Standard, 1.5 in: 4 to 24hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-32053G CLR | Teknor Apex Company | TPE | Monprene® |
| Multi-Flex® TPE A1540 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Nylene® 5143 MS | Custom Resins Group | Nylon 66 | Nylene® |
| JSR EPR EP25 | JSR Corporation | EPDM | JSR EPR |
| VALOX™ 310SE0 resin | SABIC Innovative Plastics | PBT | VALOX™ |