Celanex® 6500HF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r9YO9r_Celanex-6500HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 6500HF is a high flow, 30% glass/mineral filled polybutylene terephthalate (PBT) with improved warp resistance and surface smoothness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.80 | % | |
| Flow | 0.0 to 0.50 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.19 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 91 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Break, 23°C | 110 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Break, 23°C | 3.0 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 180 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.2 | kJ/m² | |
| 23°C | 6.7 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 24 | kJ/m² | |
| 23°C | 27 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C | 75 | J/m | ASTM D256 |
| 23°C | 5.3 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 220 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 223 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 202 | °C | ISO 75-2/A |
| Glass Transition Temperature | 54.0 | °C | ISO 11357-2 |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.8E-5 | cm/cm/°C | |
| Transverse | 8.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | |||
| -- | 1.0E+17 | ohms·cm | ASTM D257 |
| -- | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| -- 2 | 24 | kV/mm | ASTM D149 |
| -- | 31 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.30 | ||
| 1 MHz | 3.10 | ||
| Dissipation Factor (1 MHz) | 0.012 | IEC 60250 | |
| Comparative Tracking Index | 325 | V | IEC 60112 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GN1001FA | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| Varcum 29577 | Durez Corporation | Phenolic | Varcum |
| APEX® 130-P | Teknor Apex Company | PVC, Flexible | APEX® |
| Formolene® 2535A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| Novalloy-B B5526 | PlastxWorld Inc. | ABS+PBT | Novalloy-B |