CYCOLAC™ INP581 resin
| Category: | ABS+SAN , Acrylonitrile Butadiene Styrene + SAN |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r95Hr0_CYCOLACINP581resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow, low molecular weight SAN. Can be used as compounding additives for polymer blends. Can be blended with high rubber graft modifier resins to produce customized ABS properties. Suitable for direct weather exposure. Provides excellent flow for demanding injection molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 38 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 98 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4090 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 48.8 | MPa | ASTM D638 |
| Fracture | 60.2 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 1.5 | % | ASTM D638 |
| Fracture | 1.9 | % | ASTM D638 |
| Flexural Modulus | |||
| 50.0mm span 4 | 3440 | MPa | ASTM D790 |
| -- 5 | 3520 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 36.3 | MPa | ISO 178 |
| Yield, 50.0mm span 6 | 66.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -30°C | 12 | J/m | ASTM D256 |
| 23°C | 23 | J/m | ASTM D256 |
| -30°C 7 | 1.4 | kJ/m² | ISO 180/1A |
| 23°C 8 | 1.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 97.6 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 86.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 9 | 82.9 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ISO 306/B50 |
| -- | 105 | °C | ISO 306/B120 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index | 1.6 | YI | ASTM D1925 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6000 GVS 10/30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Nanjing Hongrui PP P401 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| NEFTEKHIM PP PP4340S | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| EcoVid 30GBTFH | Greener Polymers Inc. | PLA | EcoVid |
| Durethan® BM 25 FN20 700350 | LANXESS Asia/Pacific | Nylon 6 | Durethan® |