TAROBLEND 85
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROBLEND |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r8Hlig_TAROBLEND-85.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS alloy high thermal resistance, good flow and very high mechanical properties, low moisture absorption and good dimensional stability. Available: all colors, UV stabilized (L). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 to 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 to 0.70 | % | |
| Across Flow | 0.40 to 0.70 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.10 | % | ASTM D570, ISO 62 |
| Saturation | 0.40 | % | ASTM D570 |
| Saturation, 23°C | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 55.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 60 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 85.0 | MPa | ISO 178 |
| Break | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 35 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | No Break | ASTM D256, ISO 179 | |
| Notched Izod Impact | ASTM D256, ISO 180 | ||
| -30°C, 3.20 mm | 380 | J/m | |
| 23°C, 3.20 mm | 650 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature 3 | 100 | °C | IEC 60216 |
| Vicat Softening Temperature | |||
| -- | 135 | °C | ASTM D1525, ISO 306/A50 4 4 |
| -- | 125 | °C | ASTM D1525, ISO 306/B50 5 5 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Rate A (50°C/h), Loading 1 (10 N) |
| 5 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRIREX GP5500 | Formosa Plastics Corporation | PS (GPPS) | TAIRIREX |
| Calprene® H6110 | Dynasol Elastomers | SEBS | Calprene® |
| Edgetek™ CY4000-15GF/000 NC | PolyOne Corporation | PC+PBT | Edgetek™ |
| Glastherm® HT | Glastic Corporation | Polyester, TS | Glastherm® |
| ICORENE® 3933 | ICO Polymers SA, A Division of A. Schulman | LMDPE | ICORENE® |