Order Products : sales@su-jiao.com
Geon™ HTX 66311
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r83UlD_Geon-HTX-66311.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Geon™ HTX 66311 is a Polyvinyl Chloride Alloy (PVC Alloy) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Applications of Geon™ HTX 66311 include outdoor applications and wire & cable. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Spiral Flow | 86.4 | cm | |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Outdoor Suitability (All Colors) | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2410 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 41.4 | MPa | ASTM D638 |
| Flexural Modulus | 2620 | MPa | ASTM D790 |
| Flexural Strength | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| -18°C, 3.18 mm, Injection Molded | 110 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 800 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm | 76.1 | °C | |
| 0.45 MPa, Annealed, 6.35 mm | 82.2 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 72.2 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 78.9 | °C | |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI Str | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm, ALL) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 202 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LDM 760 | Marco Polo International, Inc. | LDPE | MARPOL® |
| Next Nylon 66 Prime Series PX-01GY | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Capilene® SW 75 AV | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Kingplate™ HAC8244 | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | Kingplate™ |
| Pibiflex® 4612 NATURALE | SO.F.TER. SPA | TPC-ET | Pibiflex® |