SUMILITE® PL-1187
| Category: | Phenolic , Phenolic |
| Manufacturer: | Sumitomo Bakelite Co., Ltd. |
| Trademark: | SUMILITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r702CS_SUMILITE-PL-1187.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMILITE®PL-1187 is a phenolic (Phenolic) product,. It is available in North America. SUMILITE®PL-1187 application areas include electrical/electronic applications, electrical appliances and coating applications. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Water Absorption (23°C, 24 hr) | 1.8 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength (Yield) | 130 | MPa | ASTM D790 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | 6.60 | ASTM D150 | |
| Dissipation Factor | 0.060 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Tests were performed in accordance with JIS K6911Flexural Strength, JIS K6911, Flow: 180 MpaFlexural Strength, JIS K6911, Accross Flow: 130 MpaSolvent Resistivity, JIS K6911, 30 min boil: ConstantDielectric Strength, JIS K6911, Flatwise: 18 MV/mPunching Shrinkage, JIS K6911, 60°C, 150 mm length, Flow: 0.28%Punching Shrinkage, JIS K6911, 60°C, 150 mm length, Across Flow: 0.44%Punching Temperature, JIS K6911: 130°CInsulation Resistance, JIS K6911: 1e4 M ohmsInsulation Resistance JIS K6911: 3e1 M ohmsHeat Resistivity, JIS K6911, 120 min: 120°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXAMID™ 226K6 | SAX Polymers | Nylon 66 | SAXAMID™ |
| DINALON® A1S25 G35 H | Grupo Repol | Nylon 66 | DINALON® |
| DuPure庐 R 87 E | Ducor Petrochemicals BV | PP Homopolymer | DuPure® |
| ISPLEN® PM 274 AT | REPSOL | PP Copolymer | ISPLEN® |
| Karina IVORY PVC COMPOUND 752-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |