Aristech ALTAIR PLUS® (0.275 inch)
| Category: | ABS+Acrylic , Acrylonitrile Butadiene Styrene + Acrylic (PMMA) |
| Manufacturer: | Aristech Acrylics LLC |
| Trademark: | Aristech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r6sfMg_Aristech-ALTAIR-PLUS-0-275-inch-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aristech Acrylics LLC Altair Plus® is a composite engineered material which has the exceptional surface properties, weathering characteristics and aesthetics of Aristech Acrylics LLC Opaque Continuous Cast Acrylic and a substrate that imparts outstanding impact resistance and thermoformability. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.10 | g/cm³ | ASTM D792 |
| Water Absorption (Saturation, 6.99 mm) | 0.19 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, 6.99 mm) | 97 | ASTM D785 | |
| Barcol Hardness (6.99 mm) | 52 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (6.99 mm) | 2620 | MPa | ASTM D638 |
| Tensile Strength (Yield, 6.99 mm) | 44.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 6.99 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 6.99 mm 2 | 2160 | MPa | |
| 6.99 mm 3 | 2140 | MPa | |
| Flexural Strength | ASTM D790 | ||
| 6.99 mm 4 | 74.5 | MPa | |
| 6.99 mm 5 | 68.9 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.99 mm) | 130 | J/m | ASTM D256A |
| Instrumented Dart Impact 6(6.99 mm) | > 40.7 | J | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.99 mm) | 89.4 | °C | ASTM D648 |
| CLTE - Flow (6.99 mm) | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (6.99 mm) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cycles Freeze-Thaw - 50 (-29 to 82°C, 6.99 mm) | No Effect | Internal Method | |
| Hot Forming Temperature | Internal Method | ||
| ABS Side : 6.99 mm | 149 to 171 | °C | |
| Acrylic Side : 6.99 mm | 177 to 193 | °C |
| Note Message | |
|---|---|
| 1 . | 0.275 in |
| 2 . | Acrylic in Tension |
| 3 . | Acrylic in Compression |
| 4 . | Acrylic in Tension |
| 5 . | Acrylic in Compression |
| 6 . | FTMS 406-M-1074 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 321Ss | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| ULTEM™ 2400F resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |
| Alathon® M6061 | LyondellBasell Industries | HDPE | Alathon® |
| CONAPOXY® FR-1274 | Cytec Industries Inc. | Epoxy | CONAPOXY® |
| ALCOM® PC 740/40 FR UV WT1182-10LB | ALBIS PLASTIC GmbH | PC | ALCOM® PC |