INFUSE™ 9007
| Category: | OBC , Olefin Block Copolymer |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | INFUSE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r6RyVZ_INFUSE-9007.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INFUSE™ 9007 Olefin Block Copolymer is a lower density higher performance olefin block copolymer that can be widely used in TPE applications where higher service temperature requirements are needed. INFUSE 9007 also provides high filler loading capability and gives good elastic recovery. Main Characteristics:
Complies with
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.866 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 64 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 100% Secant (Compression Molded) | 1.78 | MPa | ASTM D638 |
| Tensile Strength (Break, Compression Molded) | 4.07 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 400 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 9.70 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1300 | % | ASTM D412 |
| Tear Strength | 29.0 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 21°C | 18 | % | |
| 70°C | 57 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 119 | °C | Internal Method |
| TMA 1(1.00 mm) | 88 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 1N, 5°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MORETEC™ 0138N | Prime Polymer Co., Ltd. | LLDPE | MORETEC™ |
| NEXT REGRIND POMC TX90-100RG | NEXT Specialty Resins, Inc. | Acetal (POM) Copolymer | NEXT REGRIND |
| ExxonMobil™ SFT315 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| HIDEN® P502 YE | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Hipolyene 1046 NM | Zylog Plastalloys | TPO (POE) | Hipolyene |