STYRON™ 485
| Category: | PS (HIPS) , High Impact Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r5DSE0_STYRON-485.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ 485 is an easy-flowing, high impact polystyrene, offering high impact strength coupled with good flexibility. Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.05 | g/cm³ | ISO 1183 |
| -- | 1050 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.60 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ISO 1133 |
| Melt volume-flow rate (200°C/5.0 kg) | 12.0 | cm³/10min | ISO 1133 2 |
| Viscosity number | 59.0 | cm³/g | ISO 307, 1157, 1628 3 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 55 | ISO 2039-2 | |
| Ball Indentation Hardness | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile modulus | 2000 | MPa | ISO 527-2 4 |
| Tensile Stress | |||
| Yield | 16.0 | MPa | ISO 527-2/5 |
| Yield | 20.0 | MPa | ISO 527-2 5 |
| Break | 16.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 1.5 | % | |
| Break | 50 | % | |
| Nominal strain at break | > 50 | % | ISO 527-2 6 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Flexural Stress | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| Compression Molded | 7.0 | kJ/m² | ISO 179/2 |
| -30°C | 5.00 | kJ/m² | ISO 179/1eA 7 |
| 23°C | 7.00 | kJ/m² | ISO 179/1eA 8 |
| Charpy impact strength | ISO 179/1eU 9 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| Compression Molded | 90 | J/m | ASTM D256 |
| Injection Molded | 70 | J/m | ASTM D256 |
| -- | 28 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 88.0 | °C | ISO 75-2/B |
| 0.45 MPa | 80.0 | °C | ISO 75-2 10 |
| 1.8 MPa, Unannealed | 73.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 84.0 | °C | ISO 75-2/A |
| 1.8 MPa | 73.0 | °C | ISO 75-2 11 |
| Vicat Softening Temperature | |||
| -- | 96.0 | °C | ISO 306/A120 |
| -- | 87.0 | °C | ISO 306/B50 |
| 50°C/h, B (50N) | 87.0 | °C | ISO 306 12 |
| CLTE | ISO 11359-2 13 | ||
| Flow | 9.0E-5 | cm/cm/°C | |
| Transverse | 7.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | 1.0E+13 | ohms | IEC 60093 14 |
| Volume resistivity | > 1.0E+15 | ohms·m | IEC 60093 15 |
| Electric strength | 150 | kV/mm | IEC 60243-1 16 |
| Dielectric Constant | |||
| 1 MHz | 2.50 | ASTM D150, IEC 60250 17 | |
| 100 Hz | 2.50 | IEC 60250 18 | |
| Dissipation Factor | |||
| 1 MHz | 4.0E-4 | ASTM D150 | |
| 100 Hz | 2.0E-5 | IEC 60250 19 | |
| 1 MHz | 4.0E-5 | IEC 60250 20 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 21(1.60 mm) | HB | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm, UL) | HB | ISO 1210 22 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 700 | °C | |
| 2.00 mm | 650 | °C | |
| 3.00 mm | 650 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 22 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound G3240A | Saudi Basic Industries Corporation (SABIC) | PP Homopolymer | SABIC® PPcompound |
| Niplene F15 AGR | Soredi S.p.a. | PP Homopolymer | Niplene |
| Ad-Tech Epoxy EC-412 Medium | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| EL-Lene™ H5604F | SCG Chemicals Co., Ltd. | HDPE | EL-Lene™ |
| INEOS PP 100-GA09 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |