XYRON™ 644Z
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r45sh7_XYRON-644Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Modified PPE Unreinforced Flame retardant V-0 Heat resistance High |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.09 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.50 to 0.80 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ISO 62 |
| Outdoor Suitability (Black) | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 74.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 9.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2440 | MPa | ISO 178 |
| Flexural Stress (23°C) | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 21 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 129 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-0 | ||
| 2.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 320 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 302 TFE 15 | RTP Company | PC | RTP |
| UBESTA XPA 9055 X2 | UBE Engineering Plastics, S.A. | Nylon 12 Elast | UBESTA |
| Hanwha Total PP TB53L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| LONGLITE® PBT 3030-104FR | CCP Group | PBT | LONGLITE® PBT |
| 3M™ Dyneon™ Fluoroelastomer FC 2174 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |