Fibrolon® F 8530
| Category: | PLA , Polylactic Acid |
| Manufacturer: | FKuR Kunststoff GmbH |
| Trademark: | Fibrolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r3s3pB_Fibrolon-F-8530.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Fibrolon® F 8530 (prev. Fibrolon® B 53 AW) Biodegradable and natural fibre reinforced compound for injection moulding made primarily from renewable resources |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Apparent Density | 0.64 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 9.0 - 11 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 7.00 - 9.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 34.0 | MPa | ISO 527-2 |
| Fracture | 34.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 3.4 | % | ISO 527-2 |
| Fracture | 3.8 | % | ISO 527-2 |
| Flexural Modulus | 3700 | MPa | ISO 178 |
| Flexural Strain at Break | 3.0 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 72.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 150 - 160 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.30 | % | |
| Rear Temperature | 160 | °C | |
| Middle Temperature | 170 | °C | |
| Front Temperature | 180 | °C | |
| Nozzle Temperature | 180 | °C | |
| Processing (Melt) Temp | 170 | °C | |
| Mold Temperature | 30.0 | °C | |
| Injection Pressure | < 200 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | < 5.00 | MPa |
| Injection instructions |
|---|
| Feeding zone: 150°CCylinder kneeling temp: 140°CScrew peripheral velocity: up to 150 mm/sHolding pressure level: 40 to 70%Holding pressure time: 15 to 30 sMelt cushion (of volume): 3 to 10%Cooling time: 10 to 30 sShot volume 1 to 3 D [-] |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E Wire & Cable GA-1046CTLF | S&E Specialty Polymers, LLC | PVC, Semi-Rigid | S&E Wire & Cable |
| Adell PP RA-14 | Adell Plastics, Inc. | PP Copolymer | Adell PP |
| COPEC® CC6OCN (Series: VS/AD1) | KRAIBURG TPE | TPE | COPEC® |
| LEXAN™ GF1311R resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| Ultramid® Structure A3WG12 LFX BK23215 | BASF Corporation | Nylon 66 | Ultramid® |