Greenflex® FL 25
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Greenflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r34QZs_Greenflex-FL-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Greenflex FL 25 is an ethylene vinyl acetate copolymer (EVA) for blown film extrusion. Films produced with Greenflex FL 25 show good optical properties and ecellent sealability. Main Application Greenflex FL 25 is recommended for the production of lamination film, coextruded films and freezer bags. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Vinyl Acetate Content | 4.5 | wt% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore A, Injection Molded | 96 | ||
| Shore D, Injection Molded | 44 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.20 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 30 to 150µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : Blown Film | 140 | MPa | |
| 1% Secant, TD : Blown Film | 150 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, Blown Film | 7.00 | MPa | |
| TD : Yield, Blown Film | 7.00 | MPa | |
| MD : Break, Blown Film | 25.0 | MPa | |
| TD : Break, Blown Film | 22.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, Blown Film | 300 | % | |
| TD : Break, Blown Film | 560 | % | |
| Dart Drop Impact 1(Blown Film) | 400 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD | 25.0 | kN/m | |
| TD | 38.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -80.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 82.0 | °C | ISO 306/A |
| Melting Temperature | 103 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, Blown Film) | 87 | ASTM D2457 | |
| Haze (Blown Film) | 1.0 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| APEX® 65006 | Teknor Apex Company | PVC, Flexible | APEX® |
| LNP™ COLORCOMP™ DX06407H compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |
| LNP™ THERMOCOMP™ 2X00858 compound | SABIC Innovative Plastics | FEP | LNP™ THERMOCOMP™ |
| POLYfill PPHC TS15020 | Polykemi AB | PP, Unspecified | POLYfill |
| Sylvin 3240-65 Red 683 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |