MAJ'ECO AP404W
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJ'ECO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r2cqq6_MAJ-ECO-AP404W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJ'ECO AP404W is a 40% wood fibre reinforced polypropylene compound intended for extrusion. MAJ'ECO AP404W UV stabilised developed especially for demanding applications in various engineering sectors. APPLICATIONS Product such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 41.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.2 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3500 | MPa | ISO 178 |
| Flexural Stress 2 | 66.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 150 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 160 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Melt Temperature | 150 to 190 | °C | |
| Head Temperature | 170 | °C | |
| Die Temperature | 160 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUGUARD™ HPN469V2CSL | ACLO Compounders Inc. | PP Homopolymer | ACCUGUARD™ |
| Akulon® Ultraflow K-FHG7 /A | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| DURAFIDE® 6565A7 | Polyplastics Co., Ltd. | PPS | DURAFIDE® |
| LNP™ THERMOCOMP™ RF0069SZ compound | SABIC Innovative Plastics Asia Pacific | Nylon 66 | LNP™ THERMOCOMP™ |
| Polifor® C 30 TR/20 H GRIGIO 7306 | SO.F.TER. SPA | PP Copolymer | Polifor® |