Pebax® Rnew 35R53 SP 01
| Category: | PEBA-Ether , Polyether Block Amide |
| Manufacturer: | Arkema |
| Trademark: | Pebax® Rnew |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r27B3l_Pebax-Rnew-35R53-SP-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether block amide Pebax® Rnew 35R53 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide based on renewable resources. This SP grade has been developed to be heat and UV resistant. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 24 hr, 4.00 mm | 0.60 | % | |
| Flow : 24 hr, 4.00 mm | 0.60 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.3 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 2 | ISO 868 | ||
| Shore D | 32 | ||
| Shore D, 15 sec | 25 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3(Break) | 30.0 | MPa | ISO 527-2 |
| Tensile Strain 4(Break) | > 700 | % | ISO 527-2 |
| Flexural Modulus 5 | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 81.0 | °C | ISO 306 |
| Melting Temperature | 135 | °C | ISO 11357-3 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Renewable Carbon Conent | 28 to 32 | % | ASTM D6866 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 55.0 to 65.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Processing (Melt) Temp | 180 to 240 | °C | |
| Mold Temperature | 10.0 to 30.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 55.0 to 65.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Melt Temperature | 190 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Mold at 20°C |
| 2 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| 3 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| 4 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| 5 . | Samples conditioned 15 days at 23°C - 50 % R.H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Capran® UNIDRAW 104 | Honeywell | Nylon 6 | Capran® |
| Cheng Yu FR200GV25 | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Hangzhou Plastic PVC Rigid Film Used for Food Packaging | Hangzhou Plastic Industry Co., Ltd. | Film, PVC | Hangzhou Plastic |
| Hifax EKS 226P | LyondellBasell Industries | PP Copolymer | Hifax |
| Karina IVORY PVC COMPOUND 753D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |