MOSTEN FC 908
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | UNIPETROL RPA |
| Trademark: | MOSTEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r1UzzU_MOSTEN-FC-908.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene Mosten FC 908 is a random copolymer, intended for cast film production by chill-roll process. This product contains slip and antiblock additivation. Films produced from Mosten FC 908 exhibit outstanding transparency, gloss and very good weldability. Typical application are stationery products and various foodstuffs and textiles packaging. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 24.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 250 | % | ISO 527-2 |
| Flexural Modulus | 850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 1.5 | kJ/m² | |
| 23°C | 5.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 46.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 133 | °C | ISO 306 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MELOPAS® MF 152 | RASCHIG GmbH | Mel Formald | MELOPAS® |
| TECHNYL® A 216 S40 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| TEKNIFLEX® VPA10200 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PCTFE | TEKNIFLEX® |
| VAMPALLOY 0024 V0 12 | Vamp Tech | PC+ABS | VAMPALLOY |
| Jam HDPE HMCRP100 N | Jam Petrochemical Company | HDPE | Jam HDPE |