| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Innova SA |
| Trademark: | Innova |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r1B5Ak_Innova-N-2380E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Characteristics:
Process:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.4 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | 0.30 to 0.60 | % | |
| Water Absorption | |||
| Saturation | < 0.10 | % | ASTM D570 |
| Saturation, 23°C | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3300 | MPa | ASTM D638 |
| 23°C | 3350 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Break, 23°C | 58.0 | MPa | ASTM D638 |
| Break, 23°C | 54.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 2.3 | % | ASTM D638 |
| Break, 23°C | 2.7 | % | ISO 527-2 |
| Flexural Strength | |||
| 23°C | 95.0 | MPa | ASTM D790 |
| 23°C | 90.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 23 | J/m | ASTM D256 |
| 23°C | 2.2 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 95.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 107 | °C | ASTM D1525, ISO 306/A50 2 1 |
| -- | 102 | °C | ASTM D1525, ISO 306/B50 3 2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 210 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 1 (10 N) |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vinnolit® K 707 E | Vinnolit GmbH & Co. KG | PVC Alloy | Vinnolit® |
| Ultramid® 8202C HS | BASF Corporation | Nylon 6 | Ultramid® |
| TYNEC® CG100 | Tyne Plastics LLC. | PC | TYNEC® |
| Braskem PP CP 404XP | Braskem | PP Impact Copolymer | Braskem PP |
| Karina RED COLOR CONCENTRATE 42/228-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |