LUVOCOM® 16-8699 Datasheet,PARA,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®16-8699 is a polyacrylamide (PARA) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 16-8699 are: High stiffness high strength Wear-resistant Lubrication Typical application areas include: engineering/industrial accessories Electrical/electronic applications textile/fiber Automotive Industry business/office supplies

General Information
Filler / Reinforcement	Glass fiber reinforced material
Additive	PTFE lubricant
Features	Low friction coefficient Rigidity, high High strength Good wear resistance Lubrication
Uses	Gear Textile applications Engineering accessories Switch Application in Automobile Field Business equipment Bearing
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.51	g/cm³	ISO 1183
Molding Shrinkage	0.10 - 0.50	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.30	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	12000	MPa	ISO 527-2
Tensile Stress (Break)	185	MPa	ISO 527-2
Tensile Strain (Yield)	2.1	%	ISO 527-2
Flexural Modulus	10000	MPa	ISO 178
Flexural Stress	265	MPa	ISO 178
Coefficient of Friction
Dynamic	0.18
Static	0.15
Flexural Strain at Flexural Strength	2.8	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	170	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	50	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	230	°C	ISO 75-2/A
Continuous Use Temperature	125	°C	UL 746B

Injection	Nominal Value	Unit
Drying Temperature
B	130	°C
Hot air dryer, A	100	°C
Drying Time
B	4.0 - 6.0	hr
Hot air dryer, A	6.0 - 8.0	hr
Suggested Max Moisture	0.10	%
Rear Temperature	260 - 300	°C
Middle Temperature	260 - 300	°C
Front Temperature	260 - 300	°C
Nozzle Temperature	250 - 290	°C
Processing (Melt) Temp	285	°C
Mold Temperature	110 - 140	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PARA , Polyarylamide
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	r187zr_LUVOCOM-16-8699.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Synres-Almoco DAIP 6552	Synres-Almoco BV	DAP	Synres-Almoco
EVALENE® LLDPE LF20184	JG Summit Petrochemical Corporation	LLDPE	EVALENE® LLDPE
Laprene® 830901955	SO.F.TER. SPA	SEBS	Laprene®
Karina BLACK PVC COMPOUND -E MCP 520	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
ALTECH® PP-H FC 1000/576	ALBIS PLASTIC GmbH	PP Homopolymer	ALTECH® PP-H