RTP 200 A
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r0QIto_RTP-200-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced - UL94 V-2 (NC) - UL94 HB (All Colors) |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 1.3 - 1.7 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.9 | % | ASTM D570 |
| Moisture Content | 0.20 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2760 | MPa | ASTM D638 |
| Tensile Strength | 75.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 10 | % | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 171 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 71.1 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(in Oil) | 16 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.030 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -17.8 | °C | |
| Processing (Melt) Temp | 243 - 279 | °C | |
| Mold Temperature | 54.4 - 93.3 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 | RTP Company | Nylon 66 | RTP |
| Ming Dih EPS LS3 | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| REVOLVE® N-324 | Matrix Polymers | LMDPE | REVOLVE® |
| TRIBOCOMP® PEEK TS9 | EPIC Polymers | PEEK | TRIBOCOMP® |
| ESENTTIA 03H83-AV | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |