LNP鈩?THERMOCOMP鈩?PX85100 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | r01fqY_LNP-THERMOCOMP-PX85100-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP PX85100 is a compound based on Nylon 6 resin containing Proprietary Filler(s). Also known as: LNP* THERMOCOMP* Compound PDX-P-85100 Product reorder name: PX85100 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 10300 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break | 157 | MPa | |
| Break 2 | 157 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield 3 | 9.0 | % | |
| Break | 2.7 | % | |
| Break 4 | 2.7 | % | |
| Flexural Modulus | ASTM D790 | ||
| -- | 8030 | MPa | |
| 50.0 mm Span 5 | 8030 | MPa | |
| Flexural Strength | 228 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 1100 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 206 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ X3 ST6000-5006 FR BLACK | PolyOne Corporation | Nylon 6 | Stat-Tech™ |
| APEX® 90-U656F1-72 | Teknor Apex Company | PVC, Flexible | APEX® |
| Ferro PP NPP00GB07K | Ferro Corporation | PP, Unspecified | Ferro PP |
| Huafon JF-S-AH8045 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| ISOPAK® 525 Black | Great Eastern Resins Industrial Co., Ltd. (GRECO) | ABS | ISOPAK® |