MAJORIS EEG204 - 8229
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qzgdUY_MAJORIS-EEG204---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EEG204-8229 is a 20% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. EEG204-8229 has been developed especially for demanding applications in automotive industry and various engineering sectors. EEG204-8229 has high rigidity, good dimensional stability and good creep resistancy also at high temperatures. It has high flow rate and very good process ability. APPLICATIONS Product requiring high service temperature and extremely high mechanical strength such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Vertical flow direction | 0.95 | % | |
| Flow direction | 0.39 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3300 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 64.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 4.4 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3550 | MPa | ISO 178 |
| Flexural Stress | 102 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 162 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 134 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 - 270 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Rate | Slow-Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 525T | Salflex Polymers Ltd. | HDPE | Salflex |
| Shandong PP GFPP40-1 | Shandong Dongchen Engineering Plastics Co., Ltd. | PP, Unspecified | Shandong PP |
| Braskem PP H105-03NA | Braskem Europe GmbH | PP Homopolymer | Braskem PP |
| Eltex® P KS417 | INEOS Olefins & Polymers Europe | PP Random Copolymer | Eltex® P |
| Optix® CA-924 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |