Next ABS SXT4-02ABK
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qyg4yR_Next-ABS-SXT4-02ABK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description ABS Modified Black Compound Product Applications Automotive sector, Appliance components & Housing Application Benefits Having high impact resistance, High heat, better Flow |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | > 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.25 | % | |
| Across Flow | 0.25 | % | |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.30 | % | |
| Saturation 1 | 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2750 | MPa | ASTM D638 |
| Tensile Strength | 57.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 2800 | MPa | ASTM D790 |
| Flexural Strength | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 104 | °C | |
| Vicat Softening Temperature | 115 | °C | ASTM D1525 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 21 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | > 400 | V | UL 746 |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | 22 | sec | UL 746 |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 70.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 65.0 to 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 15 SI 2 | RTP Company | Acetal (POM) Copolymer | RTP |
| Vydyne® R515H Natural | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| GAPEX® RPP40EA35UL-NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Karina LILAC COLOR CONCENTRATE 34/ 87-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRILOY™ RX05498 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |