OmniLon™ PA6/6 IM20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniLon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qycS13_OmniLon-PA6-6-IM20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Super High Impact, Nylon 6/6 |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 51.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 45 | % | ASTM D638 |
| Flexural Modulus | 1720 | MPa | ASTM D790 |
| Flexural Strength | 65.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 216 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 71.1 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 293 | °C | |
| Middle Temperature | 271 to 293 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® RE5264 NC010 | DuPont Performance Polymers | PET | Rynite® |
| TEKNIFLEX® VA15300 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| KPOL-HDPE HD K-04/950 | KPOL Chem Co. | HDPE, HMW | KPOL-HDPE |
| Karina CLEAR PVC COMPOUND -E 75/244-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SIBUR Synthetic Rubber NBR 2665 | SIBUR | NBR | SIBUR Synthetic Rubber |