RTP EMI 863
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qxc8tk_RTP-EMI-863.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stainless Steel Fiber - Electrically Conductive - EMI/RFI/ESD Protection |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 2.0 - 3.2 | % | ASTM D955 |
| Moisture Content | 0.15 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Static Decay | sec | FTMS 101C 4046.1 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3380 | MPa | ASTM D638 |
| Tensile Strength | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 - 6.0 | % | ASTM D638 |
| Flexural Modulus | 3030 | MPa | ASTM D790 |
| Flexural Strength | 67.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 190 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 97.8 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | < 1.0E+3 | ohms | ASTM D257 |
| -- | < 1.0E+2 | ohms | ESD STM11.11 |
| Volume Resistivity | < 1.0 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 177 - 213 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Injection Pressure | 68.9 - 103 | MPa |
| Injection instructions |
|---|
| Use a reverse barrel profile. Remove hopper magnets. Allow 4 - 5 shots to properly disperse the conductive fibers. The surface finish should have a silver streaking appearance, not clumps.Use a reverse barrel profile. To maximize fiber length, the following injection barrel, screw, and tip designs should be followed. L/D ratio 16/1 - 22/1, Compression ratio 2:1, Flight depth 0.200 in (5 mm) minimum, in feed section, Screw diameter 0.65 - 0Remove hopper magnets.Desiccant Type Dryer Required. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aplax P0213GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| ARCEL® LD (2.00 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| FERREX® GPP20CG39UL WHITE | Ferro Corporation | PP Homopolymer | FERREX® |
| SABIC® PPcompound 7251U | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Durethan® BKV 215 H2.0 DUS035 900051 | LANXESS GmbH | Nylon 6 | Durethan® |