Lucel® GC240
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lucel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qxOr7U_Lucel-GC240.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUCEL GC-240 improves rigidity and conductivity by compounding actal with glass fiber. Users have various options to select grades appropriate for their application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 to 0.70 | % | |
| Across Flow | 0.30 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 87 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 148 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus 2(23°C) | 11800 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 276 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 46.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Reverse Notch Izod Impact (23°C) | 900 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 6.35 mm | 165 | °C | |
| 1.8 MPa, Annealed, 6.35 mm | 165 | °C | |
| Melting Temperature | 165 | °C | |
| CLTE - Flow (20 to 80°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 25 | kV/mm | ASTM D149 |
| Arc Resistance | 135 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.734 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Nozzle Temperature | 200 to 220 | °C | |
| Melt Temperature (Aim) | 210 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 68.6 to 118 | MPa | |
| Holding Pressure | 39.2 to 83.4 | MPa | |
| Back Pressure | 0.00 to 3.92 | MPa | |
| Screw Speed | 40 to 75 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 15 mm/min |
| 3 . | 15 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® OBC 4670A | Teknor Apex Company | TPE | Telcar® |
| Wondel® P PI0M4 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| NYCOA Polyamide 5400 | Nycoa (Nylon Corporation of America) | Nylon 66 | NYCOA Polyamide |
| Edgetek™ ET3200-8001 LG | PolyOne Corporation | PC | Edgetek™ |
| LNP™ STAT-KON™ EX07311P compound | SABIC Innovative Plastics Asia Pacific | PEI | LNP™ STAT-KON™ |