Generic PET
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qxLsAT_Generic-PET.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PET This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.25 - 1.41 | g/cm³ | ASTM D792 |
| 23°C | 1.33 - 1.43 | g/cm³ | ISO 1183 |
| -- | 1.39 - 1.40 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.84 - 0.88 | g/cm³ | ASTM D1895 |
| Bulk Density | 817 - 897 | kg/m³ | |
| Melt Mass-Flow Rate (MFR) (265°C/5.0 kg) | 14 - 60 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.26 - 1.2 | % | ASTM D955 |
| Transverse flow : 23°C | 0.67 - 1.4 | % | ASTM D955 |
| 23°C | 0.40 - 1.9 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.098 - 0.10 | % | ASTM D570 |
| 23°C, 24 hr | 0.28 - 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 - 0.31 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) (23°C) | 78.0 - 86.5 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 109 - 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1970 - 3820 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 39.3 - 147 | MPa | ASTM D638 |
| Yield, 23°C | 55.0 - 90.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 24.0 - 77.0 | MPa | ISO 527-2 |
| Tensile Strain | |||
| Yield, 23°C | 2.8 - 4.0 | % | ISO 527-2 |
| Fracture, 23°C | 2.0 - 13 | % | ASTM D638 |
| Fracture, 23°C | 1.2 - 250 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1860 - 9810 | MPa | ASTM D790 |
| 23°C | 2060 - 2330 | MPa | ISO 178 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 73.1 - 164 | MPa | ASTM D790 |
| Yield, 23°C | 68.7 - 177 | MPa | ASTM D790 |
| Compressive Stress (23°C) | 24.0 - 103 | MPa | ISO 604 |
| Coefficient of Friction | 0.30 - 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 5.1 - 57 | µm | |
| secant modulus | ASTM D882 | ||
| MD | 1650 - 3360 | MPa | ASTM D882 |
| TD | 1450 - 2180 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 173 - 207 | MPa | ASTM D882 |
| TD : Yield | 46.6 - 257 | MPa | ASTM D882 |
| MD : Fracture | 165 - 207 | MPa | ASTM D882 |
| TD : Fracture | 186 - 220 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 90 - 170 | % | ASTM D882 |
| TD : Fracture | 81 - 140 | % | ASTM D882 |
| Oxygen Permeability (23°C) | 0.700 - 0.920 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen Permeability (23°C) | 3.8 - 4.9 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission | 0.40 - 47 | g/m²/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.0 - 7.8 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 14 - 100 | J/m | ASTM D256 |
| 23°C | 2.0 - 4.6 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 63.9 - 250 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 57.8 - 230 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 74.8 - 80.0 | °C | ISO 75-2/A |
| Continuous Use Temperature | 95.3 - 164 | °C | ASTM D794 |
| Glass Transition Temperature | 70.0 - 79.0 | °C | ASTM E1356 |
| Melting Temperature | |||
| -- | 115 - 261 | °C | |
| -- | 245 - 258 | °C | DSC |
| -- | 245 - 255 | °C | ASTM D3418 |
| CLTE - Flow | |||
| -- | 3.0E-5 - 3.1E-5 | cm/cm/°C | ASTM D696 |
| -- | 6.0E-5 - 8.3E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 105 - 150 | °C | UL 746 |
| RTI Imp | 105 - 150 | °C | UL 746 |
| RTI | 103 - 154 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 - 2.5E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+14 - 2.5E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 12 - 25 | kV/mm | ASTM D149 |
| Dielectric Constant | |||
| 23°C | 3.41 - 3.83 | ASTM D150 | |
| 23°C | 3.30 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 2.0E-3 - 0.017 | ASTM D150 | |
| 23°C | 1.0E-3 - 0.014 | IEC 60250 | |
| Arc Resistance | 80.0 - 125 | sec | ASTM D495 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | 148 - 193 | ASTM D523 | |
| Gloss | 48 - 101 | ASTM D2457 | |
| Opacity | 85 - 90 | % | ASTM D589 |
| Transmittance | 87.0 - 92.1 | % | ASTM D1003 |
| Haze | 0.20 - 5.1 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 162 | °C | |
| Drying Time | 4.9 - 6.0 | hr | |
| Dew Point | -36.7 - -36.5 | °C | |
| Rear Temperature | 246 - 290 | °C | |
| Middle Temperature | 251 - 280 | °C | |
| Front Temperature | 256 - 280 | °C | |
| Nozzle Temperature | 250 - 280 | °C | |
| Processing (Melt) Temp | 277 - 280 | °C | |
| Mold Temperature | 29.6 - 135 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PETThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 127 - 170 | °C | |
| Drying Time | 5.4 - 7.0 | hr | |
| Melt Temperature | 270 - 281 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PETThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2308N0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Monprene® RG-20269 | Teknor Apex Company | TPE | Monprene® |
| Fainplast PVC MGS 89/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| EPO-TEK® 320 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| EPO-TEK® EK1000-MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |