Kingfa JH710 G30
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qx9dvl_Kingfa-JH710-G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa JH710 G30 is a polycarbonate alloy (PC alloy) material, which contains a 30% glass fiber reinforced material. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa JH710 G30 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.43 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C) | 0.20 - 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 86 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 115 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 7.0 | % | ASTM D638 |
| Flexural Modulus 3 | 8900 | MPa | ASTM D790 |
| Flexural Strength 4 | 170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 90 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 148 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 134 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.80 mm | V-0 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 80.0 - 130 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 295°CInjection Speed: 60 to 90% |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan A-9016/B-8016 | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| AKROMID® A3 GK 30 black (2306) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| ALTECH® PC A 1000/326 UV | ALBIS PLASTIC GmbH | PC | ALTECH® PC |
| Plaslube® PA6 TS18 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| XYLEX™ X8409AC resin | SABIC Innovative Plastics | PC+Polyester | XYLEX™ |