PALFORM® R H 10
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | pal plast GmbH |
| Trademark: | PALFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qwy8ly_PALFORM-R-H-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PALFORM®R H 10 is a polyoxymethylene (POM) homopolymer product,. It can be processed by injection molding and is available in Europe. Typical application areas are: engineering/industrial accessories. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 3.00 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield, 23°C) | 69.5 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield, 23°C) | 43 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break (23°C) | 23 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 159 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 178 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Melt-Volume Flow Rate, ISO 1133, 190°C/2.16 kg: 2 to 4 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2900 to 3100 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 68 to 71 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 40 to 45 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 20 to 25 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 12 to 15 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 157 to 160 °CDensity, ISO 1183: 1.4 to 1.42 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.7 to 0.9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Metocene MF650Y | LyondellBasell Industries | PP Homopolymer | Metocene |
| Tenite™ Propionate 381E4000015 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Star L PA6 D61 | Eurostar Engineering Plastics | Nylon 6 | Star L |
| Titalon® 2300CF | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Durethan® BG 60 X XF 900116 | LANXESS GmbH | Nylon 6 | Durethan® |