SABIC® PPcompound PHC25-20
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qwBUaT_SABIC-PPcompound-PHC25-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound PHC25-20 is a talc-filled copolymer for use in applications which involve high requirements in terms of stiffness, thermal dimensional stability as well as impact resistance. Typical examples of applications are dashboard carriers and console column cladding. SABIC® PPcompound PHC25-20 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 1.2 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 25.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 170 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 2200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 25 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | 24 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 4.5 | kJ/m² | |
| 0°C, Injection Molded | 6.0 | kJ/m² | |
| 23°C, Injection Molded | 15 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 145 | °C | ISO 306/A |
| CLTE - Flow (-30 to 30°C) | 9.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Torelina® A674M2 | Toray Resin Company | PPS | Torelina® |
| Vydyne® R860 BK02 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| ICORENE® 1901 | ICO Polymers EMEA, A Division of A. Schulman | Plastomer | ICORENE® |
| Sylvin 8773-60D Brown 7373 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |
| Wuxi Jiahong EB-203 | Wuxi Jiahong Plastics Technology CO., Ltd. | PVC, Unspecified | Wuxi Jiahong |