Rilsan® MB 3504 HP

Category:	Nylon 11 , Polyamide 11
Manufacturer:	Arkema
Trademark:	Rilsan®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	qvB0yC_Rilsan-MB-3504-HP.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Rilsan® MB 3504 HP is a Polyamide 11 (Nylon 11) product. It can be processed by extrusion, injection molding, or profile extrusion and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.

Characteristics include:

Eco-Friendly/Green

Good UV Resistance

Heat Stabilizer

Impact Resistant

Lubricated

General Information
Additive	Heat Stabilizer Lubricant Plasticizer
Features	Good Impact Resistance Good UV Resistance Heat Stabilized Lubricated Renewable Resource Content
Forms	Pellets
Processing Method	Extrusion Injection Molding Profile Extrusion
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1030	1030	kg/m³	ISO 1183 ¹
Melt volume-flow rate (235°C/2.16 kg)	1.00	--	cm³/10min	ISO 1133 ²

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	610	520	MPa	ISO 527-2 ³
Tensile Stress (Yield)	32.0	30.0	MPa	ISO 527-2 ⁴
Tensile Strain (Yield)	32	33	%	ISO 527-2 ⁵
Nominal strain at break	> 50	> 50	%	ISO 527-2 ⁶

Impact	Dry	Conditioned	Unit	Test Method
Charpy notched impact strength				ISO 179/1eA ⁷
-30°C	7.00	10.0	kJ/m²
23°C	55.0 kJ/m²	No Break
Charpy impact strength				ISO 179/1eU ⁸
-30°C	No Break	No Break
23°C	No Break	No Break

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa)	40.0	--	°C	ISO 75-2 ⁹
Melting Temperature ¹⁰	185	--	°C	ISO 11357-3 ¹¹
CLTE - Flow	1.4E-4	--	cm/cm/°C	ISO 11359-2 ¹²

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behav. at 1.6mm nom. thickn. (1.60 mm)	HB	--		ISO 1210 ¹³
Burning Behav. at thickness h (3.20 mm)	HB	--		ISO 1210 ¹⁴
Oxygen index	22	--	%	ISO 4589-2 ¹⁵

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	10 °C/min
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
13 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
14 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC M1399	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
Michiflex E9280A	API Polymers, Inc.	TPV	Michiflex
Zytel® HTN 51G45HSL NC010	DuPont Performance Polymers	PPA	Zytel® HTN
Plenco 04466 (Transfer)	Plastics Engineering Co.	Phenolic	Plenco
Deprene 101-73	Shanghai Lin Gen Rubber Materials Co., Ltd.	PP+EPDM	Deprene