| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Holland BV |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qtSULr_DiakonFrost95260.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon®Frost 952 60 is a polymethyl methacrylate-acrylic material,. This product is available in Europe and is processed by extrusion. Diakon®The main characteristics of Frost 952 60 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.5 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ISO 2039-2 | |
| Ball Indentation Hardness (H 961/30) | 170 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 72.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.4 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 22 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 1.6 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 99.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 108 | °C | ISO 306/A |
| -- | 101 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | ASTM D1003 | ||
| 1000 µm | 83.0 | % | ASTM D1003 |
| 1500 µm | 77.0 | % | ASTM D1003 |
| 2000 µm | 71.0 | % | ASTM D1003 |
| 2500 µm | 58.0 | % | ASTM D1003 |
| Haze | ASTM D1003 | ||
| 1000 µm | 97 | % | ASTM D1003 |
| 1500 µm | 98 | % | ASTM D1003 |
| 2000 µm | 98 | % | ASTM D1003 |
| 2500 µm | 99 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50 - 90 | °C | |
| Cylinder Zone 1 Temp. | 160 - 250 | °C | |
| Cylinder Zone 2 Temp. | 180 - 260 | °C | |
| Cylinder Zone 3 Temp. | 200 - 260 | °C | |
| Cylinder Zone 4 Temp. | 220 - 270 | °C | |
| Cylinder Zone 5 Temp. | 220 - 270 | °C | |
| Adapter Temperature | 210 - 270 | °C | |
| Die Temperature | 210 - 270 | °C |
| Extrusion instructions |
|---|
| Zone 6: 220 to 270°CZone 7: 210 to 270°CZone 8: 210 to 270°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 9156 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Sylvin 8679-50 Red 6238 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NOVADURAN® 5010GN6-30M8X | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| Nypol® PA B3 G20 PRTA011 NT307 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| Europrene® N 3945 GRN | Versalis S.p.A. | NBR | Europrene® |