Vikalloy IM62
| Category: | PMMA+PVC , Acrylic (PMMA) + PVC |
| Manufacturer: | Viking Polymers, LLC |
| Trademark: | Vikalloy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qs0B0C_Vikalloy-IM62.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vikalloy IM62 is an acrylic acid (PMMA) PVC (PMMA PVC) material,. This product is available in North America, Europe or Asia Pacific region. The processing method is injection molding. The main features of Vikalloy IM62 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 34 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 44.8 | MPa | ASTM D638 |
| Flexural Modulus | 2250 | MPa | ASTM D790 |
| Flexural Strength | 64.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 960 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, not annealed | 70.6 | °C | ASTM D648 |
| 1.8 MPa, annealed | 75.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (2.03 mm) | V-0 5VA | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 54.4 - 71.1 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Shot Size | 75 | % | |
| Middle Temperature | 157 - 196 | °C | |
| Front Temperature | 157 - 196 | °C | |
| Mold Temperature | 32.2 - 60.0 | °C | |
| Back Pressure | 0.689 - 2.76 | MPa | |
| Clamp Tonnage | 4.1 - 4.8 | kN/cm² | |
| Screw Compression Ratio | 2.0:1.0 to 2.6:1.0 |
| Injection instructions |
|---|
| Drying is typically not necessary, however if the material is old or has been stored in moist conditions follow the drying conditions listed. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMORUN® QT85MA | Mitsubishi Chemical Corporation | TPO (POE) | THERMORUN® |
| Zhongfa PC/ABS CH-110 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PC+ABS | Zhongfa |
| Baydur® 661 IBS (45 pcf, 20% Wollastocup) | Covestro - PUR | PUR-MDI | Baydur® |
| Epolene® C-16P | Westlake Chemical Corporation | LDPE | Epolene® |
| Sylvin 9077-90 Yellow 4215 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |