LNP™ STAT-KON™ OE006A compound
| Category: | PPS, Branched , Branched Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qrSsKd_LNP-STAT-KON-OE006A-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* OE006A is a compound based on PPS - Branched resin containing 30% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound OC-1006 Product reorder name: OE006A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.44 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.080 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.030 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 32800 | MPa | ASTM D638 |
| -- | 25500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 210 | MPa | ASTM D638 |
| Break | 204 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.1 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 23500 | MPa | ASTM D790 |
| -- | 24700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 305 | MPa | ASTM D790 |
| -- | 312 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 1.6 | ||
| vs. Itself - Static | 1.4 | ||
| Wear Factor - Washer | 857 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 50 | J/m | ASTM D256 |
| 23°C 2 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 28 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.30 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE | |||
| Flow : -40 to 40°C | 7.2E-6 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 8.7E-6 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.0E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.00 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 485 TFE 15 | RTP Company | PS (GPPS) | RTP |
| Sindustris ABS LHG204S | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| IROGRAN® A 85 P 4722 | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| LNP™ THERMOCOMP™ RF008XXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| CYCOLOY™ CX7720 resin | SABIC Innovative Plastics Asia Pacific | PC+ABS | CYCOLOY™ |