SCHULAFORM® 9D DB LE BLACK
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAFORM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qqwNMD_SCHULAFORM9DDBLEBLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Easy flow Polyoxymethylene grade with low emissions for automotive applications (dry blend) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 26.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2800 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 145 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 100 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 162 | °C | ISO 306/A50 |
| -- | 150 | °C | ISO 306/B50 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission of Organic Compounds | |||
| VDA 277, TVOC (total organic compounds) | µgC/g | VDA 277 | |
| VDA 278, Fog (condensable compounds) | µgC/g | VDA 278 | |
| VDA 278, VOC (volatile organic compounds) | µgC/g | VDA 278 | |
| Formaldehyde Emissions | mg/kg | VDA 275 | |
| Odor | 3.50 | VDA 270 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 200 - 210 | °C | |
| Mold Temperature | 60 - 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell 2007H | LyondellBasell Industries | LDPE | Purell |
| Michilene F8100 | API Polymers, Inc. | PP Homopolymer | Michilene |
| Shanghai Ofluorine PVDF 9201 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| APEX® 4124 | Teknor Apex Company | PVC, Flexible | APEX® |
| Dorlyl PVC GFE 65S | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |