MonoSol® M2631A
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qqb70h_MonoSol-M2631A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol M2631A is a PVOH based thermoplastic film, soluble in cold water and manufactured using MonoSol's proprietary solution cast technology. MonoSol M2631A is a cold water-soluble PVOH film engineered with greater stiffness than conventional water soluble films. This unique film is ideal for a variety of diverse applications includingimmersion graphics, water-soluble labels, and water-soluble packaging. Standard thicknesses are 40 micron (1.6 mil) and 30 micron (1.2 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 6.6 | wt% | |
| Solubility 2 | |||
| Disintegration : 10°C, 40.6 µm | 38.0 | sec | |
| Disintegration : 24°C, 40.0 µm | 17.0 | sec | |
| Dissolution : 10°C, 40.6 µm | 70.0 | sec | |
| Dissolution : 24°C, 40.6 µm | 34.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (40.0 µm) | 19.5 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 41 | µm | |
| Film Thickness - Recommended / Available | 40 µm, and 30 µm | ||
| Secant Modulus - 100%, MD | 40.0 | MPa | ASTM D882, ISO 527-3 |
| Tensile Strength - MD | |||
| Break | 77.9 | MPa | ASTM D882 |
| -- | 77.9 | MPa | ISO 527-3 |
| Tensile Elongation - MD (Break) | 340 | % | ASTM D882, ISO 527-3 |
| Elmendorf Tear Strength - MD | |||
| -- | 100 | g | ASTM D1922 |
| -- | 0.010 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mowital® B 30 T | Kuraray Co., Ltd. | PVB | Mowital® |
| Ultraform® H 2320 006 | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| XYRON™ L544V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NYCOA Polyamide 715 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Karina BLACK PVC COMPOUND 858-48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |