| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qnSZg2_Braskem-PE-EF2002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EF2002 is a low-density polyethylene (LDPE) with high molecular weight. Has excellent processability, proper of branched polyethylene produced by a high-pressure process. EF2002 resin presents an excellent performance in conventional LDPE extruders, granting low energy consumption during the whole process and allowing the production of packaging with a good dimensional uniformity and an excellent surface finishing. Application: High resistance films for industrial packaging, heavy duty bags and plastic canvas. Base resin for agriculture films with big dimensions. Process: Blown Film Extrusion |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.920 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.16 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 50 µm | 150 | MPa | ASTM D882 |
| 2% secant, TD : 50 µm | 170 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm | 30.0 | MPa | ASTM D882 |
| TD : Break, 50 µm | 25.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 360 | % | ASTM D882 |
| TD : Break, 50 µm | 740 | % | ASTM D882 |
| Dart Drop Impact 1(50 µm) | 200 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 180 | g | ASTM D1922 |
| TD : 50 µm | 200 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm) | 53 | ASTM D2457 | |
| Haze | 19 | % | ASTM D1003 |
| Extrusion instructions |
|---|
| Recommended Blow Film Extrusion Conditions: Temperature Profile: 170°C to 225°C Mass Temperature: 190°C to 225°C Blow up Ratio: 2.0 to 3.0 : 1 Die Gap: 1.0 to 1.5 mm |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 91 T 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| Ultramid® TG7S BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Hanwha Total PP FB82 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| PERLEX® R2520 | A. Schulman Europe | PC | PERLEX® |
| RTP ESD C 4580 | RTP Company | PK | RTP |