Lumid® GP2130AE
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qnIRyv_Lumid-GP2130AE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description General Purpose Applications Industrial Material |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.090 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 113 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 8.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 4410 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 195 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 MHz) | 3.80 | ASTM D150 | |
| Arc Resistance 5 | 160 | sec | ASTM D495 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 235 to 255 | °C | |
| Middle Temperature | 240 to 270 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumikon® FM-MK505 | Sumitomo Bakelite Co., Ltd. | PPS | Sumikon® |
| APEX® 3301-85NT | Teknor Apex Company | PVC, Flexible | APEX® |
| KOPA® KN133G15BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Hostacom X M2 T28 | LyondellBasell Industries | Polyolefin, Unspecified | Hostacom |
| LNP™ STAT-LOY™ A3000 compound | SABIC Innovative Plastics | ABS | LNP™ STAT-LOY™ |