POCAN® ECO T 3215 000000
| Category: | PBT+PET , Polybutylene Terephthalate + PET |
| Manufacturer: | LANXESS GmbH |
| Trademark: | POCAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qmh74C_POCANECOT3215000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT+PET, 15 % glass fibers, injection molding, improved surface finish, contains 30 % post consumer recyclat, increased temperature peak load |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.43 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 | g/cm³ | ISO 60 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 16.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 2577 | ||
| Vertical flow direction : 270°C, 2.00mm 1 | 1.0 | % | ISO 2577 |
| Vertical flow direction : 120°C, 4 hours, 2.00mm 2 | 0.20 | % | ISO 2577 |
| Flow direction : 270°C, 2.00mm 3 | 0.50 | % | ISO 2577 |
| Flow direction : 120°C, 4 hours, 2.00mm 4 | 0.10 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.40 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 180 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 110 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 5800 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | ||
| 3.5% strain, 23°C | 165 | MPa | ISO 178/A |
| 23°C 6 | 170 | MPa | ISO 178/A |
| Flexural Strain at Flexural Strength 7(23°C) | 3.8 | % | ISO 178/A |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PBT+PET, GHMR, 09-060, GF15 | ISO 7792 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.0 - 0.020 | % | Karl Fisher |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | < 10 | kJ/m² | ISO 179/1eA |
| 23°C | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 30 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | < 10 | kJ/m² | ISO 180/1A |
| 23°C | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 190 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 205 | °C | ISO 306/B50 |
| Melting Temperature 8 | 225 - 250 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 55°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Circulation Dryer | 120 | °C | |
| Drying Time - Circulation Dryer | 4.0 - 8.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 90°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 90°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 61 GB 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| Toraycon® 5174G-X11 | Toray Resin Company | PBT | Toraycon® |
| NORYL GTX™ GTX902D resin | SABIC Innovative Plastics Europe | PPE+PS+Nylon | NORYL GTX™ |
| Grilon® F 34 NL | EMS-GRIVORY | Nylon 6 | Grilon® |
| INNOPOL® PP CS 2-9120 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |