IROGRAN® A 92 E 5670 FCM
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qlaRtE_IROGRAN-A-92-E-5670-FCM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 92 E 5670 FCM is a thermoplastic polyester polyurethane for melt calendering. IROGRAN is part of the HUNTSMAN technical extrusion/injection molding product range and offers a specially designed, flexible material with a broad processing window. IROGRAN A 92 E 5670 FCM is a food contact material. PERFORMANCE FEATURES
APPLICATION
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.20 | g/cm³ | ASTM D792, DIN 53479 |
| Melt Mass-Flow Rate (MFR) (190°C/10.0 kg) | 62 | g/10 min | |
| Molding Shrinkage - Flow (Injection Molded) | 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, DIN 53505 | ||
| Shore A, Injection Molded | 91 | ||
| Shore D, Injection Molded | 37 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | |||
| -- | 20 | mm³ | DIN 53516 |
| -- | 20 | mm³ |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| TMA 3 | Internal Method | ||
| High | 170 | °C | |
| Low | 124 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Calendar Temperature Profile 4 | |||
| Front Roll (32rpm) | 170 to 190 | °C | |
| Rear Roll (27rpm) | 170 to 190 | °C |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 5(Break, 0.635 mm) | 36.0 | MPa | DIN 53504 |
| Tensile Elongation 6(Break, 0.635 mm) | 580 | % | DIN 53504 |
| Tear Strength 7(0.635 mm) | 83 | kN/m | DIN 53515 |
| Compression Set 8 | ASTM D395, DIN 53517 | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 40 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 195 | °C | |
| Cylinder Zone 2 Temp. | 195 | °C | |
| Cylinder Zone 3 Temp. | 195 | °C | |
| Cylinder Zone 4 Temp. | 195 | °C | |
| Cylinder Zone 5 Temp. | 195 | °C | |
| Adapter Temperature | 210 | °C | |
| Die Temperature | 210 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | 2 Roll Mill |
| 5 . | Extruded Film |
| 6 . | Extruded Film |
| 7 . | Extruded Film |
| 8 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5132-75UV Clear Green 3182 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| apilon 52® TL 40 | API SpA | TPU-Polyether | apilon 52® |
| Karina IVORY PVC COMP. -E 750D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PAmpellonne® 607s | Politem Plastik Ltd. | Nylon 66 | PAmpellonne® |
| Durethan® BKV 215 W1 902176 | LANXESS GmbH | Nylon 6 | Durethan® |