InnoTuf® HP-2160D
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | InnoTuf® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | qlUVCG_InnoTuf-HP-2160D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HP-216OD is a tough, abrasion resistant elastomer formulated for hand-mix processing methods. Excellent physical properties can be obtained with a room temperature cure without the utilization of mercury, MOCA, or MDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| Base Resin | 1.08 | g/cm³ | |
| Cured | 1.09 | g/cm³ | |
| Hardener | 1.19 | g/cm³ | |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D2566 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 32.0 | mg | ASTM D4060 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 18 Mix Ratio by Weight: 20 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Demold Time | 240 to 360 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.60 | Pa·s | |
| 25°C 2 | 3.3 | Pa·s | |
| 25°C 3 | 7.1 | Pa·s | |
| Curing Time (25°C) | 1.7E+2 | hr | |
| Gel Time | 20 to 30 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 55 to 65 | ASTM D2240 | |
| Tensile Strength | 34.5 | MPa | ASTM D638 |
| Tensile Elongation at Break | 280 | % | ASTM D638 |
| Tear Strength | 113 | kN/m | ASTM D624 |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Mixed |
| 3 . | Resin |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unipren® Elastomers A3 NTLA010 55A UP302 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| EPLAMID 6 GI0 15 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| INSTRUC PPSGF15 | Infinity LTL Engineered Compounds | PPS | INSTRUC |
| 3M™ Dyneon™ Fluoroelastomer FC 2122 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| RONFALIN® ABS 1363 A | A. Schulman Europe | ABS | RONFALIN® |